Rema Tiptop

PT SARANA CONVEYOREMAIL : saranagroup@cbn.net.idREMA TIP TOPWidely recognized as the world’s finest cold vulcanizing cement REMASC2000 is the solution to your industrial bonding problems. By usingREMA UTR20 hardener with the SC2000 cement natural rubber,neoprene rubber, SBR rubberand others can be bonded to each other,fabric and to steel without the aid ofheat, pressure or special equipment.DescriptionREMA SC2000 is a two component, roomtemperature curing chloroprenebased liquid rubber adhesive that, whencatalyzed with the appropriateamount of UTR20 Hardener, yieldshigh strength adhesions.  REMASC2000 is ideal for use in lininginstallations, when bonding rubber torubber, rubber to fabric, rubber to steel,rubber to concrete, fiberglass, andurethane, as well as the splicing and repair of fabric conveyor belting.Repair to existing rubber lined vessels and rubber components are alsorecommended.Mixing instructionsThe REMA SC2000 cement system iscomprised of cement and hardenerin the ratio of 1 Kg of cement to40 grams of hardener.  These twocomponents must be thoroughly mixed (stirred).  The mixed portion shouldbe used within 2 hours.General Rubber Lining Environmental ConditionsBefore any sandblasting, application of metal primer, adhesives orapplication of lining material the ambient temperature and that of thesubstrate must be at least + 50° Fahrenheit with a maximum temperatureof + 104° to +113° Fahrenheit.The Relative Humidity should notexceed 80% duringthe

PT SARANA CONVEYOREMAIL : saranagroup@cbn.net.idREMA TIP TOPWidely recognized as the world’s finest cold vulcanizing cement REMASC2000 is the solution to your industrial bonding problems. By usingREMA UTR20 hardener with the SC2000 cement natural rubber,neoprene rubber, SBR rubberand others can be bonded to each other,fabric and to steel without the aid ofheat, pressure or special equipment.DescriptionREMA SC2000 is a two component, roomtemperature curing chloroprenebased liquid rubber adhesive that, whencatalyzed with the appropriateamount of UTR20 Hardener, yieldshigh strength adhesions.  REMASC2000 is ideal for use in lininginstallations, when bonding rubber torubber, rubber to fabric, rubber to steel,rubber to concrete, fiberglass, andurethane, as well as the splicing and repair of fabric conveyor belting.Repair to existing rubber lined vessels and rubber components are alsorecommended.Mixing instructionsThe REMA SC2000 cement system iscomprised of cement and hardenerin the ratio of 1 Kg of cement to40 grams of hardener.  These twocomponents must be thoroughly mixed (stirred).  The mixed portion shouldbe used within 2 hours.General Rubber Lining Environmental ConditionsBefore any sandblasting, application of metal primer, adhesives orapplication of lining material the ambient temperature and that of thesubstrate must be at least + 50° Fahrenheit with a maximum temperatureof + 104° to +113° Fahrenheit.The Relative Humidity should notexceed 80% duringthe53535

PT SARANA CONVEYOREMAIL : saranagroup@cbn.net.idREMA TIP TOPWidely recognized as the world’s finest cold vulcanizing cement REMASC2000 is the solution to your industrial bonding problems. By usingREMA UTR20 hardener with the SC646464646462000 cement natural rubber,neoprene rubber, SBR rubberand others can be bonded to each other,fabric and to steel without the aid ofheat, pressure or special equipment.DescriptionREMA SC2000 is a two component, roomtemperature curing chloroprenebased liquid rubber adhesive that, whencatalyzed with the appropriateamount of UTR20 Hardener, yieldshigh strength adhesions.  REMASC2000 is ideal for use in lininginstallations, when bonding rubber torubber, rubber to fabric, rubber to steel,rubber to concrete, fiberglass, andurethane, as well as the splicing and repair of fabric conveyor belting.Repair to existing rubber lined vessels and rubber components are alsorecommended.Mixing instructionsThe REMA SC2000 cement system iscomprised of cement and hardenerin the ratio of 1 Kg of cement to40 grams of hardener.  These twocomponents must be thoroughly mixed (stirred).  The mixed portion shouldbe used within 2 hours.General Rubber Lining Environmental ConditionsBefore any sandblasting, application of metal primer, adhesives orapplication of lining material the ambient temperature and that of thesubstrate must be at least + 50° Fahrenheit with a maximum temperatureof + 104° to +113° Fahrenheit.The Relative Humidity should notexceed 80% duringthe64646

Adhesive CompoundsPT SARANA TEKNIK & CONVEYOR PARTREMA TIP TOP ADHESIVE SC 2000 & 4000EMAIL : SARANAGROUP@CBN.NET.ID REMA SC2000is a two component, room temperature curing chloroprene based liquid rubber adhesive that, when catalyzed with the appropriate amount of UTR20 Hardener, yields high strength adhesions. REMA SC2000 is ideal for use in lining installations, when bonding rubber to rubber, rubber to fabric, rubber to steel, rubber to concrete, fiberglass, and urethane, as well as the splicing and repair of fabric conveyor belting. Repair to existing rubber lined vessels and rubber components are also recommended.Mixing instructionsThe REMA SC2000cement system is comprised of cement and hardener in the ratio of 1 Kg of cement to 40 grams of hardener. These two components must be thoroughly mixed (stirred). The mixed portion should be used within 2 hours.General Rubber Lining Environmental ConditionsBefore any sandblasting, application of metal primer, adhesives or application of lining material the ambient temperature and that of thesubstrate must be at least + 50° Fahrenheit with a maximum temperature of + 104° to +113° Fahrenheit.The Relative Humidity should not exceed 80% during the entire lining procedure. The substrate temperature must be a minimum of 5 degrees higher than that of the dew point. Relative humidity, ambient temperature, substrate temperature and dew point must be recorded prior to start of project and at three hour intervals thereaftLEM EPOXY 4242

Adhesive CompoundsPT SARANA TEKNIK & CONVEYOR PARTREMA TIP TOP ADHESIVE SC 2000 & 4000EMAIL : SARANAGROUP@CBN.NET.ID REMA SC2000is a two component, room temperature curing chloroprene based liquid rubber adhesive that, when catalyzed with the appropriate amount of UTR20 Hardener, yields high strength adhesions. REMA SC2000 is ideal for use in lining installations, when bonding rubber to rubber, rubber to fabric, rubber to steel, rubber to concrete, fiberglass, and urethane, as well as the splicing and repair of fabric conveyor belting. Repair to existing rubber lined vessels and rubber components are also recommended.Mixing instructionsThe REMA SC2000cement system is comprised of cement and hardener in the ratio of 1 Kg of cement to 40 grams of hardener. These two components must be thoroughly mixed (stirred). The mixed portion should be used within 2 hours.General Rubber Lining Environmental ConditionsBefore any sandblasting, application of metal primer, adhesives or application of lining material the ambient temperature and that of thesubstrate must be at least + 50° Fahrenheit with a maximum temperature of + 104° to +113° Fahrenheit.The Relative Humidity should not exceed 80% during the entire lining procedure. The substrate temperature must be a minimum of 5 degrees higher than that of the dew point. Relative humidity, ambient temperature, substrate temperature and dew point must be recorded prior to start of project and at three hour intervals thereaftLEM EPOXY